AC0927 Alumina Complex Shapes, Aluminum Oxide Complex Shapes, Al2O3

Catalog No.	AC0927
Material	Al2O3
Purity	99%, 99.8%
Density	3.8~3.9 g/cm3

Alumina Complex Shape Description

Alumina complex shapes have high thermal conductivity, compressive strength, and thermal shock resistance. It also has a low thermal expansion, making it a suitable material for furnace use in the crucible, tube, and thermocouple sheath form. Alumina is high hardness and good wear resistance, making it a suitable material for ball valves, piston pumps, and deep drawing tools. In addition, it can be easily combined with metals and other ceramic materials using brazing techniques and metalizing.

Alumina Complex Shape Specifications

Composition	AL97	AL98
AL2O3 Content	97%	99.80%
Color	White	Ivory
Tensile	30 Kpsi	32 Kpsi
Flexural	55 Kpsi	60 Kpsi
Compressive	300 Kpsi	330 Kpsi
Density	3.7 g/cc	3.92 g/cc
Hardness	13.8 HV, Gpa	18 HV, Gpa
Thermal Conductivity	25 W/(m K)	32 W/(m K)
C.O.T.E.	77 In / In°C (x10^7)	78 In / In°C (x10^7)
Working Temperature	1500 °C	1750 °C
Dielectric Constant	9.5	9.8
Volume Resistivity	>10^14 Ohm-cm	>10^15 Ohm-cm
Dielectric Strength	16 KV/mm	20 KV/mm

*This chart just demonstrates the typical properties of common alumina materials we use to produce our alumina parts. Please notice that the property for customized alumina parts could vary due to different process. China Special Ceramic Parts, Inc. (CSCPI) could provide aluminum oxide ceramic products produced under your specified instruction, or do the best to meet customers’ requirements.

Alumina Complex Shape Applications

o Used for making parts for CVD, ion implants, photolithography, and semiconductor parts.
o In traditional industries, alumina ceramics are ideal for products such as injector tubes, gas nozzles and insulators.
o Alumina tubes are widely used as protector for high temperature thermal couples.

Packaging

Our Alumina ceramic complex shapes are carefully handled to prevent damage during storage and transportation and to preserve the quality of our products in their original condition.